特種光纖系列
Non-doped SMFF Loss Spectrum 非摻雜單模氟化物光纖標準參數
| Item | ZSF-9/125-N-0.20 |
Fiber Type | Step Index Type Single Mode Fiber |
NA | 0.20±0.01 |
Cut-off Wavelength(µm) | <2.6 |
Loss@1.5µm(dB/m) | <0.1 |
Core Diameter(µm) | 9±1 |
Cladding Diameter(µm) | 123±3 |
Coating Diameter(µm) | 460±30 |
Core/Cladding Glass | ZBLAN Fluoride Glass |
Coating Material | UV Curable Acrylate |
Proof Test | 1.25cm Radius |
Parameters for Custom SMFF 單模氟化物光纖定制參數
Parameters | Value |
Fiber type | Step Index Type Single Mode Fiber |
Cut-off wavelength(µm) | 0.6 ~ 2.5μm |
NA | 0.16±0.02, 0.21±0.02, 0.26±0.02 |
Core diameter(µm) | 2 ~ 12μm |
Cladding diameter(µm) | 123±3 |
Coating diameter(µm) | 460±30 |
Coating Material | UV Curable Acrylate |
Proof Test | 1.25cm Radius |
稀土參雜的SMFF光纖擁有更好的吸收效率，可用于光纖激光器、光纖放大器等器件、設備。
Parameters for Custom Rare Earth doped SMFF 定制稀土摻雜單模光纖參數
Item | RE doped Single Mode Fiber |
Fiber type | Step index type single mode fiber |
Dopant | Pr, Nd, Ho, Er,Dy, Tm, Yb, others |
Dopant concentration (ppm mol) | 500 ~ 50000 |
Numerical aparture | 0.16, 0.21, 0.26 |
Cut-off wavelength(µm) | <2.5 |
Core diameter(µm) | 2 ~ 12 |
Cladding diameter(µm) | 123±3 |
Coating diameter(µm) | 460±30 |
Core/Cladding glass | ZBLAN fluoride glass |
Coating material | UV curable acrylate |
Proof test | 1.25cm radius |
Price | $10,000 ~ $20,000/lot |
Background Loss & Emission Wavelength 背景損耗和發射波長
Non-doped MMFF Loss Spectrum 損耗圖
Non-doped MMFF Standard Specifications 非摻雜多模氟化物光纖標準參數
Item | ZMF-400/500-N-0.29 | ZMF-160/200-N-0.29 | ZMF-100/125-N-0.29 |
Fiber type | Step index type multimode fiber | ||
Core dia.(µm) | 400±25 | 160±10 | 95±5 |
Cladding dia.(µm) | 500±25 | 200±10 | 123±5 |
Coating dia.(µm) | 600±30 | 480±30 | 460±30 |
Numerical aparture | 0.29±0.01 | ||
Loss@2.5µm(dB/m) | <0.1 | ||
Core/cladding glass | ZBLAN fluoride glass | ||
Coating material | UV Curable acrylate | ||
Parameters for Custom MMFF 多模氟化物光纖定制參數
Parameters | Value |
Fiber type | Step index type multimode fiber |
Numerical aparture | 0.22±0.02, 0.27±0.02, 0.30±0.02 |
Core/cladding ratio | 80/100 |
Cladding dia.(µm) | 123±3, 200±10, 500±25 |
Coating dia.(µm) | 460±30, 480±30,600±30 |
Coating material | UV curable acrylate |
*其他參數也可定制，請聯系業務。
DCFF configurations 雙包層氟化物光纖構造圖
Parameters for Custom DCFF 稀土摻雜雙包層氟化物光纖可定制參數
| Item | RE doped Double Cladding Fiber |
Fiber Type | Double cladding fluoride fiber |
Dopant | Pr, Nd, Ho, Er,Dy, Tm, Yb, others |
Dopant concentration (ppm mol) | 500~50000 |
Cladding shape | Circular Octagonal Rectangular |
Core NA | 0.16, 0.21, 0.26 |
Cladding NA | 0.5 |
Cut-off Wavelength(µm) | <2.5 |
Core Diameter(µm) | >2 |
Cladding size(µm) | Circular:123/200/500 (diameter) Octagonal: 123/200/500 (diagonal length) Rectangular: 123/200/500 (diagonal length) |
Coating Diameter(µm) | 460, 480, 600 |
2nd cladding thickness (µm) | >30 |
2nd cladding material | fluororesin |
Coating Material | UV curable acrylate |
Proof Test | 1.25cm, 2cm, 6cm Radius |
Price | $10,000 ~ $25,000/lot |
Background Loss & Emission Wavelength背景損耗和發射波長
By selecting rare earth elements and excitation wavelengths, light emissions of various wavelengths are obtained.
While the core has low loss in the region of long wavelengths, propagation light in the first clad causes greater loss at 1.7 μm and longer wavelengths due to absorption of the fluorine-based UV resin used for the second clad.
|
|
|
|
|
|